— The results showed that the leaching process using 2M HCl could reduce crystal peaks and ball milling for 15 hours using HEM produces a sand particle size of 103.8 nm. From the XRD test of five sintering temperatures, amorphous silica occurs at a temperature of 700°C, while at other temperatures, crystalline silica peaks still appear.